樂泰 HYSOL KL-G 100 epoxy molding compoundcontains no bromine, antimony or phosphorus flame retardant.This material is designed to achieve JEDEC Level 3 requirements, at 260°C reflow temperature.
樂泰HYSOL KL-G 100 provides the lowest cost of ownership withsuperior moldability and reliability.
樂泰 HYSOL KL-G 100 meets UL 94 V-0 Flammability at6.35mm thickness.TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 20Spiral Flow, @ 175°C, cm 65ShelfLife:@5oC,days183TYPICALPROCESSDATAHandlingPreheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 20Automold, seconds 4 to 10Curing Time, @ 175oC, seconds:Conventional mold, 40 to 90Automold, 20 to 60
Post Cure @ 175°C, hours 4 to 6樂泰 HYSOL KL-G 100 has been formulated to provide the bestpossible moldability and as wide a molding latitude as possible.
Although molding and curing conditions will vary from situation tosituation, recommended starting ranges are shown above.
StorageStore product in the unopened container in a dry location.
Storage information may be indicated on the product containerlabeling.
Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers.
After removal from cold storage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.
樂泰 HYSOL KL-G 100環(huán)氧模塑料不含溴，銻或磷阻燃劑。該材料旨在實現(xiàn)JEDEC 3級要求，在260°C回流溫度。
樂泰HYSOL KL-G 100具有*低的成型成型性和可靠性.樂泰 HYSOL KL-G 100符合UL 94 V-0可燃性，厚度為6.355mm。
固化材料的特性時間175℃，秒20螺旋流， 175°C，cm 65Shelf壽命：@5oC，天183工藝流程數(shù)據(jù)處理預熱溫度：常規(guī)模具，℃80至100Automold，秒0至5模具溫度，℃150至195壓鑄壓力，Kg /cm240至100轉印時間：常規(guī)模具，秒10至20Auold，秒4至10℃，175℃，秒：常規(guī)模具，40至90Automold，20至60后固化@ 175° |